725-H53-81 Micaceous iron oxide epoxy anticorrosive coating

Product Description

-A two pack abrasion resistant epoxy anticorrosive coating giving excellent long term anticorrosive protection.

-Suitable for application at low temperature

-VOC less than 290g/L

Intended Uses

- For use in all above water areas

-For use at Newbuilding, Maintenance and Repair or On Board Maintenance

Product Information

Volume Solids

65%±2%

Finish/Sheen

Gloss

Typical Film Thickness

125 microns dry (190microns wet)

Theoretical Coverage

5.3m2/L at typical film thickness

Mix ratio

3.2:1(volume)6.5:1(mass)

Method of Application

Airless Spray

Recommended

Tip size range

0.38-0.53mm

Output pressure

≥17MPa

Air Spray

Tip size range

2.0-3.0mm

Output pressure

≥0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

-5°C     60min

5°C      30min

25°C     10min

35°C     5min

Drying Information

-5°C

5°C

25°C

35°C

Touch Dry

6h

4h

2h

1h

Hard Dry

36h

24h

18h

12h

Pot Life

6h

4h

2.5h

1.5h

Overcoating Data          Substrate Temperature

Overcoated by

-5°C

5°C

25°C

35°C

Min Max

Min Max

Min Max

Min Max

725-H53-81

36h --

24h --

18h --

12h  --

725-J43-5

36h --

24h --

18h --

12h  --

725-BS43-91

72h --

36h --

20h --

12h  --

725-H42-30

36h --

24h --

18h --

12h  --

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25°C. Subject to re-inspection thereafter

Pack Size

Part A

29.2kg/15.5L in 20 L container

Part B

4.5kg/4.5L in 6 L container

Flash Point

Part A

Greater than 31°C

Part B

Greater than 28°C

Mixed paint

Greater than 31°C

Systems and

Compatibility

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Newbuilding

Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T 8923-1988).The weld seams areas could be cleaned to St3(GB/T 8923-1988)using power tool.

Apply 725-H53-81 before oxidation occurs. If oxidation has occurred, the entire oxidized area should be reblasted to the standard specified above.

Repair/On Board Maintenance

The areas to be repaired should be cleaned to St3(GB/T 8923-1988)by  mechanical method or higher level of surface prepared to Sa2.5(GB/T 8923-1988)by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

Limitations

This product will not cure adequately below -10°C. For maximum performance ambient curing temperature should be above -5°C.

In common with all epoxy base coatings, 725-H53-81 will exhibit chalking of the firm on UV exposure.

Apply in good weather. Temperature of the surface to be coated must be least 3°C above the dew point when the humidity is lower than 85%.

The dry time and overcoating interval may change according to the environment factors.

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.